The super corrosion resistant coating of iron pot is upgraded on the basis of waterborne double layer non-stick coating, and the corrosion resistance is increased on the basis of the original performance, whcih make the product more suitable for the iron pot project.
Excellent corrosion resistance:
Excellent corrosion resistance, excellent corrosion resistance (cast iron pan)
** Boiled water test 180 h without exception coating without bubble, rust, fall off wait for a phenomenon.
** 10% brine boiling in 24 hours, no bubble, rust, fall off wait for a phenomenon.
** gb after 5 cycle corrosion test coating without bubble, rust, fall off wait for a phenomenon (in 10% salt water cook eight hours, 16 hours for a loop).
Excellent viscosity:
The topcoat has an excellent cracking film thickness and can reach 25μm without cracking (the traditional water double cracking film thickness is between 10μm-15μm), and at the same time the topcoat makes the non-sticky qualitative leap.
High wear resistance:
0.5% detergent, 3M7447B baijie cloth with weight of 4.5kg, 250 times face change after ≥ 4000 times.